【International Papers】Efficient Suppression of Persistent Photoconductivity in β-Ga₂O₃-Based Photodetectors with Square Nanopore Arrays

      Researchers from the School of Microelectronics of Shandong University have published a dissertation titled " Efficient Suppression of Persistent Photoconductivity in β-Ga₂O₃-Based Photodetectors with Square Nanopore Arrays" in ACS Publications.

Abstract

      In this work, square nanopore arrays were developed on the surface of β-Ga₂O₃ microflakes using focused ion beam (FIB) etching, and solar-blind photodetectors (PDs) were fabricated based on the β-Ga₂O₃ microflakes with square nanopore arrays. The β-Ga₂O₃ microflake-based device was transformed from a gate voltage depletion mode to an oxygen depletion mode by FIB etching. The developed device exhibited excellent solar-blind PD performance with extremely high responsivity (1.8 × 10⁵ at 10 V), detectivity (3.4 × 10¹⁸ Jones at 10 V), and light-to-dark ratio (9.3 × 10⁸ at 5 V) as well as good repeatability and excellent stability. The intrinsic mechanism responsible for this performance was then systematically discussed. This work opens up a new avenue for the fabrication of high-performance β-Ga₂O₃-based low-dimensional PDs with high reproducibility by employing the FIB etching process.

Paper Link：https://pubs.acs.org/doi/10.1021/acsami.3c05265